| Alloy Name | |||||||||||||||||||||||
| AMW32 | IS/ISO | DIN CEN/TS 13388 | UNS | JIS | KMW | ||||||||||||||||||
| CuSn5 | CuSn5 | CW451K | C51000 | C5102 | CuSn5 | ||||||||||||||||||
| Chemical Composition | (% By Weight) |
| P | 0.02 0.40% |
| Sn | 4.5-5.5% |
| Pb | 0.02 Max % |
| Zn | 0.30 Max |
| Fe | 0.10 Max % |
| Cu | Reminder % |
| Main Applications | |
| Electrical | Miniaturized Connectors, Contact Springs, Relais Springs, Terminals, Switch Parts, Fuse Clips, Electronic Connectors, Resistance Wire, Wire Brushes. |
| Fasteners | Lock Washers, Cotter Pins, Fasteners. |
| Industrial | Bellows, Textile Machinery, Perforated Sheets, Springs, Sleeve Bushing, Clutch Disks. |
| Physical Properties Typical values in annealed temper at 20°C | ||
| Density | 8.85 | g/cm3 |
| Thermal expansion coefficient −191 .. 16 / - 0 .. 300°C | 17.8/18.1 | 10-6/K/10-6/K |
| Specific heat capacity | 0.377 | J/(g.K) |
| Thermal conductivity | 96 | W/(m.k) |
| Electrical conductivity (1 MS/m = 1m/(0 mm2)) | >= 10 | MS/M |
| Electrical conductivity (IACS) | >=17.2 | % |
| Thermal coefficient of electrical resistance (0 .. 200 C) | 0.10 | 10-3/K |
| Modulus of elasticity (1GPa = 1 kN/mm2) cold formed | 110/120 | GPa / Gpa |
| Mechanical Properties (EN 1652) | ||||
| Temper | Tensile Strength Rm MPa (N/mm2) |
Yield Strength Rp0.2 MPa (N/mm2) |
Elongation Minimum A50mm % | Hardness HV |
| O (SOFT) | 310 Min | ≤ 250 | 45 Min | 85 Max |
| HA (Quater Hard) | 350 Min | ≥ 300 | 35 Min | 110 Min |
| HB (Half Hard) | 495 Min | ≥ 400 | 10 Min | 160 Min |
| HD (Hard) | 570 Min | ≥ 500 | 4 Min | 180 Min |
| HE (Extra Hard) | 645 Min | > 550 | 2 Min | 200 Min |
| HS (Spring Hard) | 690 Min | |||
Cold formability
Hot formability
Soldering
Brazing
Oxyacetylene welding
Gas shielded arc welding
Excellent
Not Recommended
Excellent
Excellent
Fair
Good